Back to Category
Flame Retardant PC
PA / Nylon
Technical Specifications
- •UL94 V-0 / V-2 Rating
- •Transparent FR Available
- •For Charger Housings
Applications
Charger HousingsPower StripsRouter HousingsLaptop HousingsE-Cigarette Shells
Technical Data Sheet (TDS)
| Property | Typical Value |
|---|---|
| Density | 1.19 - 1.23 g/cm³ |
| Melt Flow Rate (MFR) | 5 - 15 (300°C/1.2kg) g/10min |
| Tensile Strength | 55 - 65 MPa |
| Elongation at Break | 60 - 100 % |
| Flexural Modulus | 2200 - 2500 MPa |
| Izod Impact Strength | 40 - 60 kJ/m² |
| Heat Deflection Temperature (HDT) | 120 - 130 (1.82MPa) °C |
| Flame Rating | UL94 V-0 (1.5mm) / V-2 (0.8mm) |
| Appearance | Transparent / Translucent / Black Pellets |
The above data are typical values and do not constitute a specification guarantee. Please contact us for the latest product datasheet.
Processing Conditions
Drying Temperature
120°C
Drying Time
4 - 6 hours
Injection Temperature
260 - 300°C
Mold Temperature
70 - 100°C
Injection Pressure
80 - 140 MPa
Holding Pressure
50 - 90 MPa
Back Pressure
3 - 8 MPa
Screw Speed
40 - 60 rpm
Important Notes
- Avoid excessive residence time to prevent degradation
- Moisture must be ≤ 0.02%
Storage & Handling
FR PC is moisture and heat sensitive. Store sealed in dry environment. Must use desiccant drying. Avoid high-temperature storage.