PA6+30% Glass Fiber Nylon
PA / Nylon
Technical Specifications
- •Tensile Strength ≥ 170 MPa
- •High Rigidity & Dimensional Stability
- •Excellent Heat Resistance
Applications
Power Tool HousingsAutomotive PartsMechanical ComponentsChair BasesIndustrial Parts
Technical Data Sheet (TDS)
| Property | Typical Value |
|---|---|
| Density | 1.36 - 1.38 |
| Melt Flow Rate (MFR) | 8 - 20 (275°C/5kg) |
| Tensile Strength | 170 - 190 |
| Elongation at Break | 3 - 5 |
| Flexural Modulus | 8000 - 9000 |
| Izod Impact Strength | 10 - 15 |
| Heat Deflection Temperature (HDT) | 200 - 210 (1.82MPa) |
| Appearance | Natural / Black Pellets |
| Moisture Content | ≤ 0.1 |
The above data are typical values and do not constitute a specification guarantee. Please contact us for the latest product datasheet.
Processing Conditions
Drying Temperature
80 - 100°C
Drying Time
4 - 8 hours
Injection Temperature
250 - 280°C
Mold Temperature
80 - 120°C
Injection Pressure
90 - 150 MPa
Holding Pressure
60 - 100 MPa
Back Pressure
3 - 8 MPa
Screw Speed
40 - 80 rpm
Important Notes
- Use wear-resistant screw and barrel
- Moisture must be ≤ 0.1% before molding
Storage & Handling
Reinforced nylon readily absorbs moisture — must be stored sealed. Moisture level must be ≤ 0.1% after drying. Desiccant dryer recommended.