PA6 FR Reinforced
ABS Resin
Technical Specifications
- •UL94 V-0 Rating
- •High CTI Value
- •For Electrical Connectors
Applications
Electrical ConnectorsRelay BasesCircuit Breaker HousingsSwitches & SocketsLow-Voltage Appliances
Technical Data Sheet (TDS)
| Property | Typical Value |
|---|---|
| Density | 1.40 - 1.50 g/cm³ |
| Melt Flow Rate (MFR) | 5 - 15 (275°C/5kg) g/10min |
| Tensile Strength | 130 - 150 MPa |
| Elongation at Break | 2 - 4 % |
| Flexural Modulus | 7000 - 8500 MPa |
| Izod Impact Strength | 7 - 10 kJ/m² |
| Heat Deflection Temperature (HDT) | 190 - 200 (1.82MPa) °C |
| Flame Rating | UL94 V-0 (0.8mm) |
| Appearance | Natural / Black Pellets |
The above data are typical values and do not constitute a specification guarantee. Please contact us for the latest product datasheet.
Processing Conditions
Drying Temperature
80 - 90°C
Drying Time
4 - 6 hours
Injection Temperature
240 - 270°C
Mold Temperature
70 - 100°C
Injection Pressure
80 - 130 MPa
Holding Pressure
50 - 90 MPa
Back Pressure
3 - 5 MPa
Screw Speed
40 - 70 rpm
Important Notes
- Avoid excessive residence time — max 5 min at temperature
- Use corrosion-resistant screw for FR grades
Storage & Handling
FR compounds are moisture-sensitive and heat-sensitive. Store sealed away from light. Storage temperature < 35°C recommended. Use within 4 hours after drying.