PPS + 40% GF
PPS Polyphenylene Sulfide
Free samples: 5–10 kg. Trial orders: minimum 25 kg. Regular production: minimum 1,000 kg. The customer pays shipping costs.
Jinsu has not completed UL Yellow Card certification. TDS data and UL94 test results do not constitute UL recognition. If your project requires a Yellow Card, verify certification for the exact grade before approval or purchase.
Technical Specifications
- •HDT 263°C · ISO 75 · 1.82 MPa unannealed
- •Tensile Strength 140 MPa · ISO 527
- •UL94 V-0 · 1.6 / 2.0 / 3.2 mm
Applications
Technical Data Sheet (TDS) · PPS JS G8H
| Property | TestMethod | Test Condition | Typical Value |
|---|---|---|---|
| Density | ISO 1183 | 23°C | 1.67 g/cm³ |
| Molding Shrinkage | ISO 294-4 | 23°C | 0.25 - 0.7 % |
| Tensile Strength | ISO 527 | 5 mm/min | 140 MPa |
| Elongation at Break | ISO 527 | 5 mm/min | 1.5 % |
| Flexural Strength | ISO 178 | 2 mm/min | 220 MPa |
| Flexural Modulus | ISO 178 | 2 mm/min | 13500 MPa |
| Charpy Notched Impact, 23°C | ISO 180 | 23°C | 10 kJ/m² |
| Heat Deflection Temperature (1.82 MPa) | ISO 75 | 1.82 MPa, unannealed | 263 °C |
| Heat Deflection Temperature (0.45 MPa) | ISO 75 | 0.45 MPa, unannealed | - |
| UL94 Rating, 1.6 mm | UL 94 | 1.6 mm | V-0 |
| UL94 Rating, 2.0 mm | UL 94 | 2.0 mm | V-0 |
| UL94 Rating, 3.2 mm | UL 94 | 3.2 mm | V-0 |
| Surface Resistance | IEC 60093 | 1000 V | 1.00E+14 Ω |
| Dielectric Constant, 1 MHz | IEC 60250 | 1 MHz | 4.5 |
| Electric Strength | IEC 60695-2-12 | - | 19 kV/mm |
Typical values and performance ranges are provided for grade selection. Custom formulations can be adjusted to application requirements. Final properties follow the selected grade TDS and are not specification guarantees.
- Coloured grades may differ from the values above.
- Typical values are laboratory averages for reference only and are not a product specification.
Processing Conditions · PPS JS G8H
130 - 150 °C
4 - 6 h
280 - 310 °C
120 - 150 °C
0.2 - 5 MPa
- Barrel rear 290-320°C, middle 290-310°C, front 280-290°C, nozzle 290-310°C.
- Upper processing temperature limit 330°C; moderate to fast injection speed.
- Processing conditions are for reference; adjust to the machine, mould and part.
Storage & Handling
PPS absorbs little moisture but must be dried before use: 130–150°C for 4–6 h. Store sealed in a cool, dry place away from direct sunlight and rain.
Related Products
Suzhou Jinsu New Material Co., Ltd.
WhatsApp: +86 17351132569
sales@maxnmtech.com
Product Overview
PPS + 40% GF (grade PPS JS G8H) is a 40% glass-fibre reinforced polyphenylene sulfide: HDT 263°C (ISO 75, 1.82 MPa, unannealed), tensile strength 140 MPa, flexural modulus 13500 MPa, UL94 V-0 at 1.6 / 2.0 / 3.2 mm, density 1.67 g/cm³. PPS is inherently chemical- and hydrolysis-resistant with stable dimensions; 40% glass fibre further raises stiffness and heat resistance for precision parts running hot, in contact with oils, or requiring flame retardancy.
Typical uses are igniters, solenoid valves and connectors in automotive and industrial equipment. Select against your real temperature, media and wall thickness; send grade, colour, monthly volume and destination for a quote, with samples available for mould trials.
Applications in Detail
Igniters & solenoid valves
HDT 263°C and UL94 V-0 suit positions near combustion or coil heat; PPS resists fuel, engine oil and most solvents, and its dimensions shift little with temperature and humidity, holding fit accuracy for valve cores and ignition mechanisms.
Connectors & automotive electronics
High stiffness, low shrinkage (0.25–0.7%) and V-0 suit thin-wall multi-cavity connectors; dielectric constant 4.5 (1 MHz) and surface resistance 1.00E+14 Ω support electrical insulation. Validate reflow or high-temperature duty against the real temperature profile.
Pump & industrial components
PPS resists hydrolysis and most acids, alkalis and organic solvents, suiting pump housings, impellers and valve parts in hot water, coolant and chemical media. Run compatibility tests before finalising for long-term immersion or strong oxidisers.
Frequently Asked Questions
PPS+40GF or PPS+65% GF/mineral?
40GF offers 10 kJ/m² notched impact and 140 MPa tensile — relatively tougher, for igniters and connectors taking some impact. The 65% GF/mineral grade gives 14000 MPa flexural modulus and HDT 270°C — stiffer and hotter but more brittle (8 kJ/m²), for pump housings and reflectors. Choose by load and temperature.
Does PPS need drying? What melt temperature?
PPS absorbs little moisture, but drying at 130–150°C for 4–6 h is still recommended for surface quality and dimensional stability; melt 280–310°C, mould 120–150°C (higher mould temperature aids crystallinity and stability), upper limit 330°C.
What about flame and chemical resistance?
UL94 V-0 at 1.6 / 2.0 / 3.2 mm; PPS is inherently flame-retardant without halogen additives. It resists fuel, engine oil, coolant and most solvents; strong oxidising acids (e.g. concentrated nitric or sulphuric acid) and hot strong alkalis attack it — run immersion tests for the specific media.