Platable PC/ABS
PC & PC Compounds
Free samples: 5–10 kg. Trial orders: minimum 25 kg. Regular production: minimum 1,000 kg. The customer pays shipping costs.
Jinsu has not completed UL Yellow Card certification. TDS data and UL94 test results do not constitute UL recognition. If your project requires a Yellow Card, verify certification for the exact grade before approval or purchase.
Technical Specifications
- •Platable grade · For auto interiors & appliance parts
- •Charpy Notched Impact 45 kJ/m² · ISO 179 · 23°C
- •HDT 102°C · ISO 75 · 1.82 MPa unannealed
Applications
Technical Data Sheet (TDS) · PC/ABS SF65 HF
| Property | TestMethod | Test Condition | Typical Value |
|---|---|---|---|
| Density | ISO 1183 | 23°C | 1.14 g/cm³ |
| Melt Flow Rate | ISO 1133 | 260°C, 2.16 kg | 7 g/10min |
| Molding Shrinkage | ISO 2577 | 23°C | 0.5 - 0.7 % |
| Tensile Strength | ISO 527 | 50 mm/min | 50 MPa |
| Elongation at Break | ISO 527 | 50 mm/min | ≥50 % |
| Flexural Strength | ISO 178 | 2 mm/min | 80 MPa |
| Flexural Modulus | ISO 178 | 2 mm/min | 2200 MPa |
| Charpy Notched Impact, 23°C | ISO 179 | 23°C | 45 kJ/m² |
| Charpy Notched Impact, -30°C | ISO 179 | -30°C | 30 kJ/m² |
| Heat Deflection Temperature (1.82 MPa) | ISO 75 | 1.82 MPa, unannealed | 102 °C |
| Heat Deflection Temperature (0.45 MPa) | ISO 75 | 0.45 MPa, unannealed | - |
| UL94 Rating, 1.6 mm | UL 94 | 1.6 mm | HB |
| UL94 Rating, 2.0 mm | UL 94 | 2.0 mm | HB |
| UL94 Rating, 3.2 mm | UL 94 | 3.2 mm | HB |
| Surface Resistance | IEC 60093 | 1000 V | 1.00E+16 Ω |
| Comparative Tracking Index | IEC 60112 | Solution A | - |
| Glow-Wire Flammability Index, 1.5 mm | IEC 60695-2-12 | 1.5 mm | 750 °C |
Typical values and performance ranges are provided for grade selection. Custom formulations can be adjusted to application requirements. Final properties follow the selected grade TDS and are not specification guarantees.
- Coloured grades may differ from the values above.
- Typical values are laboratory averages for reference only and are not a product specification.
Processing Conditions · PC/ABS SF65 HF
90 - 100 °C
3 - 4 h
260 - 270 °C
60 - 90 °C
- Barrel rear 230-255°C, middle 250-270°C, front 250-270°C, nozzle 250-270°C.
- Upper processing temperature limit 270°C; medium back pressure; moderate to fast injection speed.
- Processing conditions are for reference; adjust to the machine, mould and part.
Storage & Handling
PC/ABS is moisture sensitive. Store sealed in a dry environment. Dry at 90–100°C for 3–4 h before use; avoid high-temperature storage. For plated parts keep surfaces clean — mould-release residue can weaken coating adhesion.
Related Products
Suzhou Jinsu New Material Co., Ltd.
WhatsApp: +86 17351132569
sales@maxnmtech.com
Product Overview
Platable PC/ABS (grade SF65 HF) is a polycarbonate/ABS alloy developed for electroplating: platable, heat resistant and high impact, with notched Charpy 45 kJ/m² (ISO 179, 23°C) and 30 kJ/m² at -30°C, HDT 102°C (1.82 MPa, unannealed) and UL94 HB. It combines PC's heat resistance with ABS's processability and takes a decorative metal finish, suiting automotive interiors, appliance parts and electrical components that need a plated surface.
Plating adhesion depends on part surface condition, pre-treatment and the plating line, so validate on your actual process. Values here are base-resin typicals; coloured grades may differ. Send grade, colour, monthly volume and destination for a quote; samples are available for trial plating.
Applications in Detail
Plated automotive interior parts
For door handles, trim, grilles and badges needing a metal look. 45 kJ/m² notched impact and HDT 102°C meet in-car temperature and assembly loads; before plating confirm no mould-release residue and gate positions away from cosmetic faces to secure adhesion and appearance.
Appliance components
For washer panels, air-conditioner trim and kitchen-appliance handles needing decorative plating. PC/ABS's balanced stiffness and surface quality suit painting and plating; UL94 HB is a general appliance rating — choose halogen-free FR PC/ABS if the product requires flame retardancy.
Electrical parts
For switch panels, socket decorative frames and controller housings. Surface resistance 1.00E+16 Ω and GWFI 750°C (1.5 mm) support general electrical insulation and glow-wire needs; for higher electrical-safety classes validate on the finished part against the target standard.
Frequently Asked Questions
How is platable PC/ABS different from standard PC/ABS?
The platable grade is formulated for surface polarity and plating adhesion so electroless/electroplated layers bond firmly; standard PC/ABS tends to peel if plated directly. SF65 HF here offers 45 kJ/m² notched impact and HDT 102°C, balancing decorative plating and structural strength. Adhesion still depends on pre-treatment and the plating line — run a trial first.
What should I watch before plating?
Keep part surfaces clean, free of mould-release and oil residue; place gates and weld lines away from cosmetic plated faces; follow the plating line's degreasing, etching and sensitizing/activating pre-treatment. Dry the base resin at 90–100°C for 3–4 h, melt 260–270°C, mould 60–90°C to reduce internal stress and avoid post-plating blistering.
Is this grade flame retardant? Can it be used where FR is required?
No. SF65 HF is UL94 HB — a decorative plating grade without a flame-retardant package. If the part needs V-0, choose halogen-free FR PC/ABS (SF75 HF, V-0 at 1.6 mm); there is currently no flame-retardant grade of this platable PC/ABS; if the part must be both plated and V-0, contact us to discuss the requirement.