PA6+15%GF Tangguh
PA / Nylon
PA6 GF15 tangguh B3G3XH: tarik 110 MPa, modulus lentur 4800 MPa, impak bertakik 15 kJ/m². Kaku sekaligus tahan benturan untuk komponen struktural perkakas listrik, rel laci kulkas dan sepatu ski. Minta TDS dan penawaran.
Sampel gratis 5–10 kg. Pesanan percobaan minimum 25 kg. Produksi reguler minimum 1.000 kg. Biaya pengiriman ditanggung pelanggan.
Jinsu belum menyelesaikan sertifikasi UL Yellow Card. Data TDS dan hasil uji UL94 bukan pengakuan UL. Jika proyek memerlukan Yellow Card, verifikasi sertifikasi grade yang tepat sebelum persetujuan atau pembelian.
Spesifikasi Teknis
- •B3G3XH · PA6+15%GF tangguh
- •110 MPa · ISO 527
- •4800 MPa · ISO 178
- •15 kJ/m² impak bertakik · ISO 179
Aplikasi
Lembar Data Teknis (TDS) · PA6+15GF tangguh B3G3XH
| Properti | Metode Pengujian | Kondisi Pengujian | Nilai Tipikal |
|---|---|---|---|
| Densitas | ISO 1183 | 23°C | 1.21 g/cm3 |
| Kekuatan Tarik | ISO 527 | 5 mm/min | 110 MPa |
| Perpanjangan Putus | ISO 527 | 5 mm/min | 3% |
| Kekuatan Lentur | ISO 178 | 2 mm/min | 170 MPa |
| Modulus Lentur | ISO 178 | 2 mm/min | 4800 MPa |
| Kekuatan impak Charpy bertakik | ISO 179 | 23°C | 15 kJ/m2 |
| Suhu Defleksi Panas (HDT) · 1,82 MPa | ISO 75 | tanpa anil | 180°C |
| Peringkat Api | UL 94 | 3.2 mm | HB |
Nilai tipikal dan rentang kinerja menjadi acuan pemilihan grade. Formulasi khusus dapat disesuaikan dengan kebutuhan aplikasi. Sifat akhir mengacu pada TDS grade yang dipilih dan bukan jaminan spesifikasi.
- Tabel ini hanya berlaku untuk B3G3XH. Untuk grade lain gunakan TDS masing-masing.
- Nilai tipikal dari lembar data grade yang disebutkan merupakan acuan pemilihan, bukan sifat universal atau jaminan pembelian. Konfirmasikan warna, spesimen, dan kondisi uji grade yang ditawarkan.
Kondisi Pemrosesan · B3G3XH
100–120°C
4–6 h
220–230°C
80–100°C
Penyimpanan & Penanganan
PA6 tangguh diperkuat serat kaca sangat higroskopis — simpan tertutup di lingkungan kering. Kadar air ≤ 0,1% setelah pengeringan; pengering desikan disarankan.
Produk Terkait
Suzhou Jinsu New Material Co., Ltd.
WhatsApp: +86 17351132569
sales@maxnmtech.com
Aplikasi Detail
Rumah perkakas listrik
Structural power-tool parts must survive drops and being stepped on while staying stiff at screw bosses, snap fits and motor mounts. Fully toughened PA6 is too soft and creeps under bolt preload, while PA6+30GF is brittle under low-to-moderate temperature impact. B3G3XH's 15% glass gives enough boss and snap-fit strength, and its 15 kJ/m² notched impact covers drop tests from -10°C to ambient.
Rel laci kulkas
Slides are long, thin parts that live or die on dimensional stability: moisture swelling or uneven shrinkage makes drawers drag and rattle. B3G3XH shrinks only 0.4–0.9% and the glass phase holds the sliding gap in a cold cabinet, while the toughening phase keeps the edge from chipping when a drawer is overloaded or slammed shut. Run a mold temperature of 80–100°C for even crystallisation.
Sepatu ski dan komponen struktural suhu rendah
Ski boot buckles, shell reinforcements and binding parts flex repeatedly below -20°C, and brittle fracture is the dominant failure mode. The glass phase keeps loaded areas from deforming, the toughener absorbs impact energy, and together they cut the low-temperature fracture risk. Dry below 0.1% before molding — moist material cracks more readily in the cold.
Pertanyaan Umum
Bisakah PA6+15GF tangguh menggantikan PA66+GF30?
In some cases, but not blindly. PA66+GF30 is stiffer and more heat resistant, with HDT often above 240°C, whereas B3G3XH is rated 180°C at 1.82 MPa. Where service temperature stays below 120°C and the priorities are drop resistance and dimensional stability, B3G3XH is more economical and tougher; near heat sources or for long-term heat resistance, stay with PA66.
Apakah 15% serat kaca cukup, kenapa tidak 30%?
More glass means more stiffness and heat resistance but lower notched impact and more visible fibre bloom. PA6 at 30% glass typically shows 12–15 kJ/m² notched impact and cracks more readily in large housings during drops. 15% is the balance point for parts that carry load and take impact, such as housings, slides and boot shells.
Perlu dikeringkan sebelum pencetakan?
Yes. PA6 is highly hygroscopic, and moisture above 0.1% causes silver streaks, exposed glass and lost impact strength. Dry at 100–120°C for 4–6 hours per the TDS with a desiccant dryer, and feed the material as soon as drying finishes.