PA6-MK600G30
Product name: PA6-GF30
Material characteristics:
30% glass fiber reinforced PA6；High mechanical strength; Thermal stability
Typical Data Sheet：
|
ITEM（23℃） |
METHOD |
UNIT |
Test Data |
|
Physical and chemical properties |
|||
|
Density |
ISO 1183 |
g/cm³ |
1.36 |
|
Molding shrinkage |
ISO 294 |
% |
0.2-0.6 |
|
Flammability rating |
UL-94 |
Class |
HB |
|
Mechanical properties |
|||
|
Tensile Strength |
ISO 527 |
MPa |
160 |
|
Elongation at break |
ISO 527 |
% |
3 |
|
Flexural strength |
ISO 178 |
MPa |
230 |
|
Flexural modulus |
ISO 178 |
MPa |
7000 |
|
Charpy Impact Strength(Notched) |
ISO 179 |
kJ/m² |
16 |
|
Charpy Impact Strength |
ISO 179 |
kJ/m² |
95 |
|
Electrical properties |
|||
|
Surface resistivity |
IEC60093 |
Ω |
1.00E+14 |
|
Volume resistivity |
IEC60093 |
Ω.cm |
1.00E+15 |
|
Thermal properties |
|||
|
HDT（1.82MPa） |
ASTM D648 |
℃ |
205 |
|
Injection molding process |
|||
|
Pre-drying |
temperature |
℃ |
80-120 |
|
Time |
h |
4-5 |
|
|
Mold temperature |
80-90℃ |
||
|
Barrel temperature |
Front temperature |
Processing temp |
Rear temperature |
|
240-245℃ |
240-250℃ |
230-240℃ |
Applications: Machine Parts；Sports Equipment；Electrical parts